ASTM
|
| Service Recommendations |
| Carbon Steel | ASTM A216 Grade WCB | Non-corrosive applications including water, oil and gases at temperatures between -20°F (-30°C) and +800°F (+425°C) |
Low Temp Carbon Steel | ASTM A352 Grade LCB | Low temperature applications to -50°F (-46°C).Not for use above +650°F (+340°C). |
Low Temp Carbon Steel | ASTM A352 Grade LC1 | Low temperature applications to -75°F (-59°C). Not for use above +650°F (+340°C). |
Low Temp Carbon Steel | ASTM A352 Grade LC2 | Low temperature applications to -100°F (-73°C). Not for use above +650°F (+340°C). |
| 3.1/2% Nickel Steel | ASTM A352 Grade LC3 | Low temperature applications to -150°F (-101°C). Not for use above +650°F (+340°C). |
| 1.1/4%Chrome 1/2% Moly Steel | ASTM A217 Grade WC6 | Non-corrosive applications including water, oil and gases at temperatures between -20°F (-30°C) and +1100°F (+593°C). |
| 2.1/4%Chrome | ASTM A217 Grade C9 | Non-corrosive applications including water, oil and gases at temperatures between -20°F (-30°C) and +1100°F (+593°C). |
5%Chrome 1/2% Moly | ASTM A217 Grade C5 | Mild corrosive or erosive applications as well as non-corrosive applications at temperatures between -20°F (-30°C) and +1200°F (+649°C). |
9%Chrome 1% Moly | ASTM A217 Grade C12 | Mild corrosive or erosive applications as well as non-corrosive applications at temperatures between -20°F (-30°C) and +1200°F (+649°C). |
12% Chrome Steel | ASTM A487 Grade CA6NM | Corrosive application at temperatures between -20°F (-30°C) and +900°F (+482°C). |
| 12% Chrome | ASTM A217 Grade CA15 | Corrosive application at temperatures up to +1300°F (+704°C) |
| 316SS | ASTM A351 Grade CF8M | Corrosive or either extremely low or high temperature non-corrosive services between -450°F (-268°C) and +1200°F (+649°C). Above +800°F (+425°C) specify carbon content of 0.04% or greater. |
| 347SS | ASTM 351 Grade CF8C | Primarily for high temperature, corrosive applications between -450°F (-268°C) and +1200°F (+649°C). Above +1000°F (+540°C) specify carbon content of 0.04% or greater. |
| 304SS | ASTM A351 Grade CF8 | Corrosive or extremely high temperatures non-corrosive services between -450°F (-268°C) and +1200°F (+649°C). Above +800°F (+425°C) specify carbon content of 0.04% or greater. |
| 304L SS | ASTM A351 Grade CF3 | Corrosive or non-corrosive services to +800F (+425°C). |
| 316L SS | ASTM A351 Grade CF3M | Corrosive or non-corrosive services to +800F (+425°C). |
| Alloy-20 | ASTM A351 Grade CN7M | Good resistance to hot sulfuric acid to +800F (+425°C). |
| Monel | ASTM 743 Grade M3-35-1 | Weldable grade. Good resistance to corrosion by all common organic acids and salt water. Also highly resistant to most alkaline solutions to +750°F (+400°C). |
| Hastelloy B | ASTM A743 Grade N-12M | Is well suited for handling hydrofluoric acid at all concentrations and temperatures. Good resistance to sulphuric and phosphoric acids to +1200°F (+649°C). |
| Hastelloy C | ASTM A743 Grade CW-12M | Good resistance to span oxidation conditions. Good properties at high temperatures. Good resistance to sulphuric and phosphoric acids to +1200°F (+649°C). |
| Inconel | ASTM A743 Grade CY-40 | Very good for high temperature service. Good resistance to spanly corrosive media and atmosphere to +800°F (+425°C). |
| Bronze | ASTM B62 | Water, oil or gas: up to 400°F. Excellent for brine and seawater service. |